Description
ECP 210 is a magnetic compound based on special blends of magnetic additive compounded into PP in such a way as to optimise physical and magnetic properties during processing. Normally supplied as a blue coloured or natural pelleted compound.
APPLICATIONS
ECP 210 is recommended for packaging, handling, transportation applications where magnetic detection requirements exist.
PROPERTIES
Specific Gravity 0.92 g cm-3
Flexural modulus 1102 MPa
Flexural strength 25.4 Mpa
Izod Impact Strength (notched) 23.8 kJm-2
Tensile Strength 21.7 Mpa
Elongation @ break 175.4 %
RECOMMENDED PROCESSING CONDITIONS
MACHINE
It is recommended that an in-line reciprocating screw machine be used to injection mould ECP 210 but it is possible to process this material on plunger injection moulding machines.
EXTRUSION
Normal extrusion equipment should be used.
CYLINDER TEMPERATURE
220 – 230 °C depending on the size and complexity of the moulding.
MOISTURE
It is recommended that ECP 210 be dried prior to extrusion. Excess moisture may show as an inferior surface finish. Typically 2/4 hours at 80°C is adequate. Store in a warm dry place to avoid moisture.
USE OF REGRIND
Runners, sprues and scrap mouldings can be reground and blended with virgin material. Regrind additions should not exceed 10% by weight of the virgin material; otherwise some reduction in properties may be experienced.
DO NOT USE A MAGNETIC SEPARATOR IN THE MOULDING MACHINE AND HOPPER, THE GRAINS WILL SEPARATE AND STICK TO THE MAGNET!!
INFORMATION IN THIS PUBLICATION AND OTHERWISE SUPPLIED TO USERS IS BASED UPON OUR GENERAL EXPERIENCES AND IS GIVEN IN GOOD FAITH, BUT BECAUSE OF THE PARTICULARS WHICH ARE OUTSIDE OUR KNOWLEDGE AND CONTROL AND AFFECT THE USE OF THE PRODUCT, NO WARRANTY IS GIVEN OR IS IMPLIED WITH RESPECT TO SUCH INFORMATION. FREEDOM FROM PATENT RIGHTS MUST NOT BE ASSUMED.